The magnetic properties in an Fe-20Mo-5Ni-0.12C alloy, hot-rolled, solution treated at
 1230°C and aged at 610°C for
different times were measured. These properties were compared with those of the
 same alloy previously cold-rolled,
solution treated at the same temperature and aged under the same conditions.